Steel
Steel
According to DIN EN 10020:2000–07, the term steel describes a material in which the iron content exceeds the content of all other elements. Its carbon content is generally below 2.06% and it does contain other elements. However, there are exceptions to this rule, e.g. CPM-10V (2.45% carbon) or ZDP-189 with a full 3% carbon. Steel needs a minimum carbon content of 0.22% to be hardened.
| Name | % Origin | % Carbon | % Chrome | % Molybdenum | % Vanadium | % Manganese | % Nickel | % Silicon | % Cobalt | % Copper | % Phosphorus | % Nitrogen | % Niob | % Wolfram | Rockwell (HRC) |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| 1095 | USA | 0,9-1,03 | – | – | – | 0,3-0,5 | – | – | – | – | – | – | – | – | 56-59 |
| 12C27 | Sweden | 0,58 | 14 | – | – | 0,35 | – | 0,35 | – | – | – | – | – | – | 57-59 |
| 14C28N | Sweden | 0,62 | 14 | – | – | 0,6 | 0,2 | 0,03 | 0,11 | 55-62 | |||||
| 154CM | USA | 1,05 | 14 | 4 | 0,4 | – | 0,35 | – | – | – | – | – | – | 58-59 | |
| 3Cr13MoV | China | 0,26-0,4 | 12-14 | – | – | 1 | – | – | – | – | 0,04 | – | – | – | 52-55 |
| 4034 | Germany | 0,42-0,5 | 12,5-14,5 | – | – | 1 | – | 1 | – | – | – | – | – | – | 54-55 |
| 40X10C2M | Russia | 0,45 | 10 | 0,7-0,9 | 0,2 | 0,5-0,7 | 0,6 | 1,9-2,6 | – | 0,3 | 0,03 | – | – | – | 57-58 |
| 4116 | Germany | 0,45-0,55 | 14-15 | 0,5-0,8 | 0,1-0,2 | 0 | – | 0 | – | – | – | – | – | – | 55-56 |
| 420 | USA | 0,4-0,5 | 12-14 | – | – | – | – | – | – | – | – | – | – | – | 54 |
| 440A | USA | 0,6-0,75 | 16-18 | 0,75 | – | 1 | – | 1 | – | – | – | – | – | – | 56 |
| 440B | USA | 0,75-0,95 | 16-18 | 0,75 | – | 1 | – | 1 | – | – | – | – | – | – | 56 |
| 440C | USA | 0,95-1,2 | 16-18 | 0,75 | – | 1 | – | 1 | – | – | – | – | – | – | 58 |
| 5160 | USA | 0,56-0,64 | 0,7-0,9 | – | – | 0,75-1 | – | 0,15-0,3 | – | – | 0,04 | – | – | – | 56-59 |
| 5Cr15MoV | China | 0,45 | 15 | 0,5 | – | 1 | – | 1 | – | – | – | – | – | – | 55-56 |
| 8Cr13MoV | China | 0,8 | 13 | 0,15 | 0,1 | 0,4 | 0,2 | 0,5 | – | – | 0,02 | – | – | – | 58-60 |
| 95X18 | Russia | 0,9-1,1 | 17-19 | – | – | 0,8 | 0,6 | 0,8 | – | 0,3 | 0,03 | – | – | – | 57-58 |
| 9Cr18MoV | China | 0,9-1,05 | 16-19 | – | – | 0,8 | – | 0,8 | – | – | 0,03 | – | – | – | 56-58 |
| Acuto+ | 0,9-0,95 | 17-18 | 1,3-1,5 | 0,1-0,25 | 0,5 | – | 0,5 | – | – | 0,04 | – | – | – | 59-60 | |
| ATS-34 | Japan | 1,05 | 14 | 4 | – | 0,4 | – | 0,35 | – | – | – | – | – | – | 58-59 |
| AUS-4 | Japan | 0,4-0,45 | 13-14,5 | – | – | 1 | 0,4 | 1 | – | – | 0,4 | – | – | – | 55-57 |
| AUS-6 (= 6A) | Japan | 0,55-0,65 | 13-14,5 | – | 0,1-0,25 | 1 | – | 1 | – | – | – | – | – | – | 56-57 |
| AUS-8 (= 8A) | Japan | 0,7-0,75 | 13-14,5 | 0,1-0,3 | 0,1-0,25 | 1 | – | 1 | – | – | – | – | – | – | 57-58 |
| C75 | Germany | 0,7-0,8 | – | – | – | 0,6-0,8 | – | 0,15-0,35 | – | – | 0,04 | – | – | – | 55-58 |
| CPM-10V | USA | 2,45 | 5,25 | 1,3 | 9,75 | 0,5 | 0,9 | – | – | – | – | – | – | 60-64 | |
| CPM-3V | USA | 0,8 | 7,5 | 1,3 | 2,75 | – | – | – | – | – | – | – | – | – | 62-63 |
| CPM-D2 | USA | 1,55 | 11,5 | 0,9 | 0,8 | – | – | – | – | – | – | – | – | – | 59-61 |
| CPM-M4 | USA | 1,4 | 4 | 5,25 | – | 0,3 | – | 0,55 | – | 0,06 | – | – | – | 5,5 | 60-62 |
| CPM-S-30V | USA | 1,45 | 14,5 | 2 | 4 | – | – | – | – | – | – | – | – | – | 58 |
| CPM-S-35VN | USA | 1,38 | 14 | 2 | 3 | 0,5 | – | 0,5 | – | – | – | 0,05 | 0,5 | – | 59-60 |
| CPM-S-60V | USA | 2,15 | 17,5 | 0,5 | 5,75 | 0,5 | – | 0,5 | – | – | – | – | – | – | 57-58 |
| CPM-154 | USA | 1,05 | 14 | 4 | – | 0,5 | – | 0,3 | – | – | – | – | – | – | 58-61 |
| Cronidur-30 | Germany | 0,25-0,35 | 14-16 | 0,85-1,1 | – | 0-1 | 0-0,5 | 0-1 | – | – | – | 0,3-0,5 | – | – | 58-60 |
| CTS 204P | USA | 1,9 | 20 | 1 | 4 | 0,3 | – | 0,6 | – | – | – | – | – | – | |
| CTS 20CP | USA | 2,2 | 13 | 1,3 | 9,3 | 0,5 | – | 0,9 | – | – | – | – | – | – | |
| CTS 40CP | USA | 1,7 | 18 | 1 | 3 | 0,3 | – | 0,8 | – | – | – | – | – | – | |
| CTS B52 | USA | 0,98-1,1 | 1,3-1,6 | – | – | 0,25-0,45 | – | 0,15-0,3 | – | – | – | – | – | – | |
| CTS B75P | USA | 1,1-1,2 | 14-15 | 3,8-4,2 | 1-1,5 | 0,5 | – | 0,3 | – | – | – | – | – | – | |
| CTS BD-1 | USA | 0,9 | 15,5 | 0,3 | 0,1 | 0,6 | – | 0,37 | – | – | – | – | – | – | |
| CTS BD-30P | USA | 1,5 | 14 | 2 | 4 | 0,5 | – | 0,3 | – | – | – | – | – | – | |
| CTS XHP | USA | 1,6 | 16 | 0,8 | 0,45 | 0,5 | 0,35 | 0,4 | – | – | – | – | – | – | |
| D2 | USA | 1,5 | 12 | 1 | 1 | 0,6 | 0,3 | 0,6 | – | – | – | – | – | – | 59-61 |
| Elmax | USA | 1,7 | 18 | 1 | 3 | 0,3 | – | 0,8 | – | – | – | – | – | – | |
| GIN-1 | Japan | 0,9 | 15,5 | 0,3 | – | 0,6 | – | 0,37 | – | 0,03 | 0,02 | – | – | – | 56-58 |
| H1 | Japan | 0,15 | 14-16 | 0,5-1,5 | – | 2 | 6-8 | 3-4,5 | – | – | 0,04 | 0,1 | – | – | 58-59 |
| N690 | Austria | 1,07 | 17,3 | 1,1 | 0,1 | 0,4 | – | 0,4 | 1,5 | – | – | – | – | – | 58-60 |
| N695 | Austria | 0,95-1,2 | 16-18 | 0,75 | – | 1 | – | 1 | – | – | – | – | – | – | 57-58 |
| Niolox (1.4153) | Germany | 0,8 | 12,7 | 1,1 | 0,9 | – | – | – | – | – | – | – | 0,7 | – | 58-62 |
| O1 | 0,95 | 0,5 | – | 0,2 | 1,2 | – | 0,4 | – | – | 0,3 | – | – | 0,5 | 61-63 | |
| S70 | USA | 0,45-0,55 | 3-3,5 | 1,3-1,8 | 0,2-0,3 | 0,2-0,8 | – | 0,2-1 | – | – | – | – | – | – | 60-62 |
| SGPS | Sweden | 1,4 | 15 | 2,8 | 2 | 0,4 | – | 0,5 | – | – | 0,03 | – | – | – | 62 |
| SK-5 | Japan | 0,9-1 | – | 0,3 | – | – | – | 0,3 | – | – | – | – | – | – | 57-60 |
| SK-85 | Japan | 0,8-0,9 | 0 -0,3 | – | – | 0,1-0,5 | 0-0,25 | 0,1-0,35 | – | 0-0,25 | 0,03 | – | – | – | 57-60 |
| Sleipner | Sweden | 0,9 | 7,8 | 2,5 | 0,5 | 0,5 | 0,9 | >60 | |||||||
| T6MoV | France | 0,6 | 14,2 | 0,65 | 0,1 | – | 0,23 | – | – | – | – | – | – | – | 54-56 |
| VG-10 | Japan | 0,95-1,05 | 14,5-15,5 | 0,9-1,2 | 0,1-0,3 | 0,5 | – | 0,6 | 1,3-1,5 | – | 0,3 | – | – | – | 58-60 |
| VG-2 | Japan | 0,6-0,7 | 13-15 | 0,1-0,2 | – | 0,5 | 0,15 | 0,5 | – | – | 0,03 | – | – | – | 57-58 |
| X-15T.N. | France | 0,4 | 15,5 | 2 | 0,3 | – | – | – | – | – | – | 0,2 | – | – | 58 |
| X50CrMoV15 | Germany | 0,45-0,55 | 14-15 | 0,5-0,8 | 0,1-0,2 | 0 | – | 0 | – | – | – | – | – | – | 55-56 |
| ZDP-189 | Japan | 3 | 20 | – | – | – | – | – | – | – | – | – | – | – | 65-67 |
| Name | % Origin | % Carbon | % Chrome | % Molybdenum | % Vanadium | % Manganese | % Nickel | % Silicon | % Cobalt | % Copper | % Phosphorus | % Nitrogen | % Niob | % Wolfram | Rockwell (HRC) |